Structural Rearrangements of Polylactide/Natural Rubber Composites during Hydro- and Biotic Degradation

In the work, the impact of the biological medium and water on structural rearrangements in pure polylactide and polylactide/natural rubber film composites was studied. Polylactide/natural rubber films with a rubber content of 5, 10, and 15 wt.% were obtained by the solution method. Biotic degradation was carried out according to the Sturm method at a temperature of 22 ± 2 °C. Hydrolytic degradation was studied at the same temperature in distilled water. The structural characteristics were controlled by thermophysical, optical, spectral, and diffraction methods. Optical microscopy revealed the surface erosion of all samples after exposure to microbiota and water. Differential scanning calorimetry showed a decrease in the degree of crystallinity of polylactide by 2–4% after the Sturm test, and a tendency to an increase in the degree of crystallinity after the action of water was noted. Changes in the chemical structure were shown in the spectra recorded by infrared spectroscopy. Due to degradation, significant changes in the intensities of the bands in the regions of 3500–2900 and 1700–1500 cm−1 were shown. The X-ray diffraction method established differences in diffraction patterns in very defective and less damaged regions of polylactide composites. It was determined that pure polylactide hydrolyzed more readily under the action of distilled water than polylactide/natural rubber composites. Film composites were more rapidly subjected to biotic degradation. The degree of biodegradation of polylactide/natural rubber composites increased with the rise in the content of natural rubber in the compositions.


Introduction
The degradation of polymers in aqueous media is a multifactorial process studied in physics, chemistry, and biology. Polylactide (PLA) and its degradation have attracted the attention of researchers for decades [1][2][3][4]. The use of new fillers and the creation of new polymer composites always left the question of biotic and abiotic degradation open.
Considering the process of biodegradation of polymers, it must be taken into account that this is not a monoprocess but a complex system of chemical and biological interactions, which may include hydrolysis and the action of enzymes secreted by microorganisms. There are also certain characteristics of the polymers themselves that affect the biodegradation process such as molecular weight and crystallinity. The high molecular weight and high crystallinity of PLA results in slower degradation [5,6].
The biodegradability and characteristics of the environment where the biodegradation process takes place are also of great importance. Unlike other biodegradable polymers, which degrade primarily in a single step by microbial attack, PLA degradation follows a sequential mechanism [7,8]. The first step involves reducing the molecular weight of PLA • the diffusion of water into the material; • the hydrolysis of chains in the amorphous region due to the lower resistance to water; • the reducing of molecular weight due to the hydrolytic cleavage of side bonds and the formation of water-soluble compounds; • the hydrolysis of the crystalline phase, which can occur by an autocatalytic mechanism due to acidic decomposition products as well as due to an increase in the concentration of carboxylic acid at the end of the chain.
The hydrolysis process is influenced by both external and internal factors. Important external factors are the temperature and pH of the medium.
It is known that an increase in temperature can accelerate the process of hydrolytic degradation. The temperature below which the PLA hydrolytic degradation rate decreases is 60 • C [19]. At a temperature of 37 • C, the rate of degradation is reduced by about two orders of magnitude compared with the process taking place at a temperature equal to or higher than 60 • C. This effect is associated with the transition of polylactide from a glassy to a highly elastic state, and the glass transition temperature of PLA is in the range of 58-63 • C.
In addition, such changes in the rates of hydrolytic degradation also occur in systems of mixtures of PLA with another component. For example, in a mixture of polylactide and polylactic-glycolic acid (in a ratio of 50:50), the rate of hydrolytic degradation under neutral conditions increases significantly at a process temperature above 60 • C [19].
The pH value is also important. It significantly affects the destruction of PLA since it affects not only the reaction mechanism but also the kinetics of the process. Destruction in an alkaline medium begins with a nucleophilic attack on the terminal hydroxyl of another carbonyl group. As a result of this process, oligomers of lactic acid and lactide are formed, which are degraded to lactic acid [20]. In an acidic environment, the destruction of polylactide is initiated by the protonation of the terminal ester group, after which an intramolecular hydrogen bridge is formed. The products of hydrolytic degradation by this mechanism are lactic acid and lactic acid oligomers [20]. As pH values increase from 1 to 10, the observed constant first decreases, reaching a minimum around pH 4, and then increases at higher pH values. At the same time, the growth of the constant is very significant-by about four orders of magnitude. The presence of a minimum in the dependence of the kinetic constant on pH confirms that hydrolysis is catalyzed either by an acidic or alkaline medium [19]. One of the most important internal factors is the crystallinity of the polymer [2,4]. The crystalline regions of PLA are resistant to hydrolysis due to the limited access of water molecules to the chains within the solid crystalline region. This causes selective hydrolytic chain cleavage in amorphous regions and the removal of water-soluble oligomers and monomers [21]. An increase in the concentration of D-units in PLA reduces optical purity and regularity, which leads to greater diffusion of water through the polymer matrix in amorphous regions and accelerated hydrolysis [21,22].
In a sample of complete amorphous PLA, a higher degree of destruction is observed in comparison with semicrystalline PLA under the same conditions [19,21]. A decrease in the molecular weight of amorphous PLA by 14% is observed after 18 weeks of being in a phosphate-buffered solution at pH = 4 and at a temperature of 37 • C. At the same time, it will take about 20 months to reduce the molecular weight of semi-crystalline PLA by the same value and under the same conditions [19].
Plasticizers and fillers also affect the process of PLA hydrolytic degradation. The reasons for the acceleration of the process may be the presence of a phase boundary, an increase in the proportion of the amorphous phase in the composite, and the hydrophilicity of the filler.
Rubbers are often used to increase the elasticity of brittle polymers [23][24][25]. Rubbers increase elongation at break and toughness of composites [24,26]. Natural rubber (NR) is an elastomer obtained from the sap of rubber trees. The application of NR makes it possible to improve some of the mechanical properties of PLA composites and preserve the bioavailability of the resulting material [27].
Most of the works are devoted to the study of morphological features and mechanical properties of PLA/NR. The structure changes of these composites during a degradation have not been sufficiently studied. It is expected that the natural rubber used in the current work will increase the rate of PLA hydro-and biotic degradation due to an increase in the proportion of the amorphous phase in the composites and the bioavailability of NR. The DSC method was used to determine the phase transition temperatures and the degree of crystallinity. Morphology was studied by optical microscopy. Changes in the chemical and physical structure were recorded by spectral methods and X-ray diffraction, respectively.
Film samples were obtained from a solution. The polymer solutions were prepared by dissolving PLA and PLA/NR in the right ratio in 100 mL of chloroform (Component-Reactiv, Moscow, Russia). The sample weight was 9 g per 100 mL, and the ratio of the components (PLA:NR, wt.%) was 100:0, 95:5, 90:10, and 85:15. The resulting samples were dried at 40 • C for 2.5 h to remove residual solvent.

Analysis of Crystallization
Thermal analysis was performed by differential scanning calorimeter (DSC) using a DSC 204 F1 device (Netzsch, Selb, Germany) under a nitrogen atmosphere. Samples of about 5.0-5.4 mg, sealed in aluminum pans, were heated from room temperature to 200 • C at a rate of 10 • C/min. Indium with T m = 156.6 • C was used as a calibrant. The crystallinity of PLA (χ c ) was estimated from the first heating cycle using the following equation: where ∆H m is the enthalpy of melting during heating, and ∆H m * is the enthalpy assuming 100% crystalline PLA homopolymer 93.1 J/g [28].

FTIR Spectroscopy
The IR spectra were recorded on a Bruker Lumos IR Fourier device (Bruker Corp., Bremen, Germany) at a temperature of (21 ± 2) • C in the range of wave numbers 4000-400 cm −1 . The analysis was carried out by attenuated total reflection (ATR) using a diamond crystal.

Morphology
The nonwoven fabrics' morphologies were examined using an Olympus BX3M-PSLED (Tokyo, Japan) optical microscope of 200× in reflected light.

Biotic Degradation
The tests for the biodegradation of the samples under the action of soil microorganisms were carried out using a microbiological installation for the accelerated determination of biodegradation (modified Sturm method) (ISO 14855-1:2012).
The installation consisted of 18 parallel lines, twelve of which contained the analyzed samples, and the test temperature was 22 ± 2 • C. Each line consists of an air pump, six 500 mL Drexel bottles each, and a 1000 mL round bottom flask. Air was passed through the pump from left to right along each of the lines. In the first two Drexel flasks containing a concentrated (6 N) solution of sodium hydroxide, carbon dioxide was fixed from the air. The third and subsequent Drexel flasks contained a 0.05 N solution of Ba(OH) 2 . The tests were carried out for 90 days.
The air purified from carbon dioxide entered the reaction flask, which contained 500 mL of liquid soil inoculum with the test sample. The flask is closed from direct sunlight to avoid errors associated with the photosynthesis process. The soil inoculum preparation process used repeated filtration of the aqueous soil solution to get rid of the presence of protozoa in the solution.
The viability of bacteria, the presence of spores, and the absence of protozoa in the soil inoculum were analyzed using optical microscopy on a Micromed Polar 3 ToupCam 5.1 MP microscope (Micromed, St. Petersburg, Russia) at a magnification of 1000×.
During the operation of the biodegradation plant, carbon dioxide was continuously released by the microbiota in the reaction flask. The released carbon dioxide was captured in the fourth Drexel flask according to the reaction: As a result of this reaction, the pH of the medium in the flask decreased from 8.5 to 8.0.
To determine the amount of barium hydroxide reacted, a sample from the flask was titrated with 0.1 N hydrochloric acid to the equivalence point. The reaction of neutralization of barium hydroxide with hydrochloric acid is presented below: Based on the results of titration, carbon dioxide emission curves were constructed for each of the lines. Lines in which only the inoculum was present served as the baseline in the calculations. Lines in which starch was used as a biodegradable component served to confirm the viability of the microbiota. The percentage of biodegradation of a sample of polymeric material was calculated by the amount of released carbon relative to its content in the original sample.

Water Test
For testing, square-shaped film samples with a side of 25 mm were used. The test was carried out on three samples of each composition at temperature T = 22 ± 2 • C. The samples were placed in a vessel with distilled water, taken in an amount of at least 8 cm 3 Polymers 2023, 15,1930 5 of 15 per 1 cm 2 of the sample surface. The test samples did not come into contact with each other and were completely covered with distilled water. The test was carried out for 90 days.

X-ray Diffraction
An X-ray diffraction(Moscow, Russia) study of PLA based films was carried out in the Emanuel Institute of Biochemical Physics using an X-ray diffractometer of local design [29,30], supplied with the optical focusing of the X-ray beam and a linear positionsensitive X-ray detector. A fine-focus-sealed Cu X-ray tube with Ni β-filter was used as an X-ray source. The cross section of the X-ray beam in the plane of the sample was 4 × 0.15 mm 2 . X-ray detector was installed with an inclination toward the sample at~20 • , the sample to detector distance was 92 mm, and the width of the detector window was restricted with a slit to be 4 mm in order to diminish the smearing of X-ray diffraction patterns. X-ray diffraction intensity was measured in the transmission mode in the range of the diffraction vector module 0.08 nm -1 < S < 6 nm -1 , corrected for background scattering and normalized in such a way that the maximal intensity value observed at S ≈ 1.87 nm -1 had the value of 100 (S = 2sinθ/λ; 2θ: scattering angle; λ: X-ray wavelength; equal for CuKα radiation to 0.1542 nm).

Statistical Processing
The experimental results were calculated as the arithmetic mean and its standard error. The calculations were performed using Statistica 8.0 software (Dell Software Inc., Round Rock, TX, USA) and Microsoft Excel 2007.

Results and Discussion
The degradation of PLA by a generally accepted two-step mechanism first involved abiotic factors then biotic factors. The abiotic process, i.e., the chemical hydrolysis of PLA in the presence of water, after which biotic degradation occurs, in which microorganisms decompose polymer degradation products to form carbon dioxide, water, and biomass under aerobic conditions and methane, hydrocarbons, and biomass under anaerobic conditions [31][32][33].
The biodegradation of PLA and PLA/NR composites was studied by the Sturm method. After 90 days of the experiment at room temperature, it was determined that the degree of biodegradation ( Figure 1) was proportional to the content of NR in the composites. The highest values were obtained for the composition containing 15 wt.% NR. This result was due to two reasons. First, NR is known to be degraded by enzymes. Microorganisms that destroy NR are widely distributed in the environment. Many bacterial strains have been studied that are able to use NR as the sole source of carbon and energy [34]. There are works on the study of the biochemical mechanism of the biological decomposition of natural rubber [35,36]. It was shown how easily raw NR became biodegradable under the influence of soil microorganisms. Thus, the weight loss of the NR film sample in wet laboratory soil for 90 days was 38 wt.% [37]. The highest values were obtained for the composition containing 15 wt.% NR. This result was due to two reasons. First, NR is known to be degraded by enzymes. Microorganisms that destroy NR are widely distributed in the environment. Many bacterial strains have been studied that are able to use NR as the sole source of carbon and energy [34]. There are works on the study of the biochemical mechanism of the biological decomposition of natural rubber [35,36]. It was shown how easily raw NR became biodegradable under the influence of soil microorganisms. Thus, the weight loss of the NR film sample in wet laboratory soil for 90 days was 38 wt.% [37].
Secondly, PLA/NR composites are heterogeneous systems in which there is always an interface or an interfacial layer [38]. The interfacial layer and near-boundary regions are characterized by a reduced density compared to the component phases. Materials with such a structure are more actively attacked by aggressive media, thus composites can break down faster than pure polymers [27,39].
As for PLA, many studies have shown its slow degradation at room temperature. The process of the abiotic factors and biodegradation of PLA actively proceeds at a temperature above its glass transition temperature, since flexibility and water absorption increase, accelerating both hydrolysis and microbial attachment [19,40].
The structure and properties of the samples were controlled by DSC, X-ray, optical microscopy, and FTIR spectroscopy.
In Figure 2, images of initial samples (the inserts) and samples after biodegradation are shown. Changes in the morphologies of the composites are observed: crevices, cracks, and dark spots. The process of degradation of polymers always starts from the surface. When significant damage is formed in the structure of the surface layers, cracks penetrate the bulk of the material. At this stage, the properties of polymers deteriorate because the reactions of the decomposition of molecular chains proceed in the polymer matrix [24,41]. XRD tests were performed in all samples to study the structural changes after bio degradation. Figure 3a presents the XRD patterns of the initial samples. The degree o crystallinity of PLA/NR composites is higher than that of pure PLA (Figure 3a, curve 1). XRD tests were performed in all samples to study the structural changes after biodegradation. Figure 3a presents the XRD patterns of the initial samples. The degree of crystallinity of PLA/NR composites is higher than that of pure PLA (Figure 3a, curve 1). XRD tests were performed in all samples to study the structural changes after degradation. Figure 3a presents the XRD patterns of the initial samples. The degr crystallinity of PLA/NR composites is higher than that of pure PLA (Figure 3a It can be seen that all films have a diffraction peak at S = 1.87 nm −1 and two w peaks at S = 2.14 and 2.78 nm −1 , which are related to the α-form of crystallized PLA [42 Then, XRD analysis was carried out in the damaged spot of the film composites an It can be seen that all films have a diffraction peak at S = 1.87 nm −1 and two weak peaks at S = 2.14 and 2.78 nm −1 , which are related to the α-form of crystallized PLA [42,43]. Then, XRD analysis was carried out in the damaged spot of the film composites and the less destroyed region (Figure 3b). Figure 3b shows the patterns of the 85PLA/15NR sample, and a similar relation is observed for all composites. As a result of processing the samples by the Sturm method, for their main part, which does not contain visible macroscopic defects, the degree of crystallinity and the crystalline form of PLA change little, but, judging by the rising in the intensity of small-angle X-ray scattering at S < 0.2 nm -1 , the nanoscale inhomogeneity of their structure increases. The diffraction pattern obtained from the region with a macroscopic film defect (Figure 3b, curve 3) indicates not only an increase in the nanoscale inhomogeneity of its structure but also a significant decrease in the degree of crystallinity in this region of the film compared to the main part without such defects.
In order to gain information about thermophysical properties, the film composites were also investigated using DSC. In Figure 4, the thermograms of the samples are represented. In total, 100% PLA has a cold crystallization peak, thus the degree of crystallinity, calculated as the difference between the enthalpies of melting and cold crystallization, is less than the χ value of PLA composites ( Table 1). The DSC results are in agreement with the X-ray data. less destroyed region (Figure 3b). Figure 3b shows the patterns of the 85PLA/15NR sample, and a similar relation is observed for all composites. As a result of processing the samples by the Sturm method, for their main part, which does not contain visible macroscopic defects, the degree of crystallinity and the crystalline form of PLA change little, but, judging by the rising in the intensity of small-angle X-ray scattering at S < 0.2 nm -1 , the nanoscale inhomogeneity of their structure increases. The diffraction pattern obtained from the region with a macroscopic film defect (Figure 3b, curve 3) indicates not only an increase in the nanoscale inhomogeneity of its structure but also a significant decrease in the degree of crystallinity in this region of the film compared to the main part without such defects. In order to gain information about thermophysical properties, the film composites were also investigated using DSC. In Figure 4, the thermograms of the samples are represented. In total, 100% PLA has a cold crystallization peak, thus the degree of crystallinity, calculated as the difference between the enthalpies of melting and cold crystallization, is less than the χ value of PLA composites ( Table 1). The DSC results are in agreement with the X-ray data.      26 30 According to the DSC curves, when NR is added to the PLA matrix, the cold crystallization peak disappears. This is associated with an increase in the total amount of the amorphous phase in the composites and, probably, with an increase in the segmental mobility of macromolecules [27]. In the presence of NR, PLA molecular chains have time to fit into domains and form a crystalline structure that does not require recrystallization.
The shift of T cc towards a lower temperature could be attributed to a decrease in the molecular weight and rupture of the PLA macrochains [44]. However, in the current work, an inverse relationship was observed: in the process of degradation, the T cc of PLA increased.
The glass transition temperature (T g ) of PLA/NR composites becomes difficult to determine (values are given in brackets). The T g values of PLA/NR composites are 2-3 • C higher than 100% PLA ones. After degradation for 90 days, the glass transition temperature of PLA disappears in all PLA/NR composites (Figures 4 and 5). This behavior could be explained by the effect of plasticization [45]. Luo et al. observed the disappearance of the cold crystallization peak of PLA composites after 135 days of hydrolytic degradation [45]. The glass transition temperature (Tg) of PLA/NR composites becomes difficult to determine (values are given in brackets). The Tg values of PLA/NR composites are 2-3 °C higher than 100% PLA ones. After degradation for 90 days, the glass transition temperature of PLA disappears in all PLA/NR composites (Figures 4 and 5). This behavior could be explained by the effect of plasticization [45]. Luo et al. observed the disappearance of the cold crystallization peak of PLA composites after 135 days of hydrolytic degradation [45]. After biotic and hydrolytic degradation, the melting point of PLA decreases. Water has a greater effect on PLA Tm than the microbiota. It would seem that the polymer should break down faster in the process of biodegradation. However, it is known that the activity of the microbiota increases at temperatures of 30 °C or more [46,47], while PLA undergoes hydrolytic cleavage at an ambient temperature, and the process accelerates by increasing the temperature.
According to Table 1, the trend in the change in the degree of crystallinity is also different. After the Sturm test, the PLA degree of crystallinity decreases in all samples by 2-4%. After the action of distilled water, there is a tendency to increase the degree of PLA crystallinity. These are interesting results of the degradation of heterogeneous systems that require further investigation at various temperatures.
Changes in the chemical structure of PLA and PLA composites were studied by FTIR-ATR spectroscopy. Analysis of IR spectra of PLA/NR composites ( Figure 6) showed a high absorption intensity in the region of 1740-1080 cm −1 , which corresponded to different vi- After biotic and hydrolytic degradation, the melting point of PLA decreases. Water has a greater effect on PLA T m than the microbiota. It would seem that the polymer should break down faster in the process of biodegradation. However, it is known that the activity of the microbiota increases at temperatures of 30 • C or more [46,47], while PLA undergoes hydrolytic cleavage at an ambient temperature, and the process accelerates by increasing the temperature.
According to Table 1, the trend in the change in the degree of crystallinity is also different. After the Sturm test, the PLA degree of crystallinity decreases in all samples by 2-4%. After the action of distilled water, there is a tendency to increase the degree of PLA crystallinity. These are interesting results of the degradation of heterogeneous systems that require further investigation at various temperatures.
Changes in the chemical structure of PLA and PLA composites were studied by FTIR-ATR spectroscopy. Analysis of IR spectra of PLA/NR composites ( Figure 6) showed a high absorption intensity in the region of 1740-1080 cm −1 , which corresponded to different vibrations of polylactide fragments [48][49][50]. As a result of exposure to soil bacteria, the intensity of structure-sensitive bands decreased for almost all samples. In the region of 1380-1000 cm −1 , where the active C-O-groups were located, the absorption intensity decreased due to the disintegration of ester groups as a result of the degradation process. In the 1450 cm −1 region, related to asymmetric vibrations of the methyl group CH 3 -referring to PLA, a change in intensity was also observed [48].
It is worth mentioning that the greatest change in the absorption intensity occurred for the sharp peak in the 1750 cm −1 region, which belongs to the valent vibrations of the C=O carbonyl group in the aliphatic ethers. This fact clearly indicates the disintegration of the polylactide phase in all samples under the action of the soil environment [49].
The intensity of the structure-sensitive band 755 cm −1 , related to the -C-C-oscillations of the polylactide crystalline phase, decreased, confirming its destruction in the process of microorganism acting [50]. The reduction in the intensity of the 755 cm −1 band correlated with the DSC results. After the Sturm experiment, the PLA degree of crystallinity decreased (Table 1). It should be mentioned that the 870 cm −1 band, corresponding to -C-C-vibrations of the polylactide amorphous phase, overlapped with the 836 cm −1 peak, related to the C-H vibrations of the (CH 3 )C=CH-rubber molecule group. The decrease in absorption intensity in this region proved the degradation of both the PLA and NR.
With the increase in the NR content in the composites, the appearance of two peaks in the interval 1660-1500 cm −1 was observed. This is the result of microorganism interaction with a natural rubber molecule leading to C-N and N-H amide groups formation, while their vibrations increased the absorption intensity in this region [51]. The authors of the study on the biodegradation process of polyethylene/natural rubber (PE/NR) blends [37] also observed the appearance of bands in this region. In PE/NR samples, as well as in the studied samples, the intensity of bands in the region of 1660-1500 cm −1 increased with the rising NR content.
In addition, a broad band appeared in the region of 3500-3000 cm −1 corresponding to bound and single vibrations of the -OH groups. They were formed as a result of the chain oxidation under the influence of oxogenases on the polymer sample. As the concentration of natural rubber in the composites increased, the intensity of vibrations in this region enhanced significantly, since the rubber molecule underwent easier splitting due to its amorphous structure [52]. The disintegration of NR could be traced in the proton NMR spectra ( Figure S1).
As mentioned above, distilled water and microbiota affected the process of the disintegration of PLA/NR composites in different ways. In contrast to the Sturm test in the region of 3500-3100 cm −1 , a slight increase in the intensity of the band was observed only for PLA (Figure 7a), which referred to the formation of -OH groups during hydrolysis. After exposure to water, peaks at 1657 and 1540 cm −1 were not traced for PLA/NR composites, and there was a slight increase in intensity in this region only for 100% PLA (Figure 7b).
In the spectrum of pure PLA, the intensity of the band at 1750 cm −1 decreases (Supplementary File). Adding natural rubber changes the dependency. In the spectra of all PLA/NR composites, the intensity of the band at 1750 cm −1 increased. This meant that the formation of C=O groups of acids and esters during degradation prevailed over the process of elimination of PLA ester groups when NR added.
The morphologies of the samples also changed. The PLA/NR film composites became muddy. This result was not surprising. Many authors observed a similar effect [2,3,6,10,45]. It is known that oligomers, dimers, and lactic acid are formed (Figure 8) in the process of PLA hydrolytic degradation, which cause a loss of transparency. It is worth mentioning that the greatest change in the absorption intensity occurred for the sharp peak in the 1750 cm −1 region, which belongs to the valent vibrations of the C=O carbonyl group in the aliphatic ethers. This fact clearly indicates the disintegration of the polylactide phase in all samples under the action of the soil environment [49].
The intensity of the structure-sensitive band 755 cm −1 , related to the -C-C-oscillations of the polylactide crystalline phase, decreased, confirming its destruction in the process of microorganism acting [50]. The reduction in the intensity of the 755 cm −1 band correlated with the DSC results. After the Sturm experiment, the PLA degree of crystallinity decreased (Table 1). It should be mentioned that the 870 cm −1 band, corresponding to -C-C-vibrations of the polylactide amorphous phase, overlapped with the 836 cm −1 peak, related to the C-H vibrations of the (CH3)C=CH-rubber molecule group. The decrease in absorption intensity in this region proved the degradation of both the PLA and NR.
With the increase in the NR content in the composites, the appearance of two peaks in the interval 1660-1500 cm −1 was observed. This is the result of microorganism interaction with a natural rubber molecule leading to C-N and N-H amide groups formation, while their vibrations increased the absorption intensity in this region [51]. The authors of the study on the biodegradation process of polyethylene/natural rubber (PE/NR) blends [37] also observed the appearance of bands in this region. In PE/NR samples, as well as in the studied samples, the intensity of bands in the region of 1660-1500 cm −1 increased with the rising NR content.
In addition, a broad band appeared in the region of 3500-3000 cm −1 corresponding to bound and single vibrations of the -OH groups. They were formed as a result of the chain oxidation under the influence of oxogenases on the polymer sample. As the concentration of natural rubber in the composites increased, the intensity of vibrations in this region enhanced significantly, since the rubber molecule underwent easier splitting due to its amorphous structure [52]. The disintegration of NR could be traced in the proton NMR spectra ( Figure S1).
As mentioned above, distilled water and microbiota affected the process of the disintegration of PLA/NR composites in different ways. In contrast to the Sturm test in the region of 3500-3100 cm −1 , a slight increase in the intensity of the band was observed only for PLA (Figure 7a), which referred to the formation of -OH groups during hydrolysis. Summarizing the results, the influence of microbiota and water, even at ambient temperature, on PLA and PLA/NR composites becomes evident. Despite a low degree of biodegradation, the morphologies and structures of the samples changed, which was recorded by various methods. In the middle of the 20th century, in the works of J.A. Manson, L.H. Sperling, V.N. Kuleznev, and other authors, the features of the structures and the properties of heterogeneous polymer systems were studied. Definitely, these scientists did not work with biodegradable polymers, but, nevertheless, the patterns remained the same. Stresses were formed at the polymer1-polymer2 interface due to different viscosities, thermal expansion coefficients of the components, the chemical nature of the polymers, and other parameters. As a result, very often polymer blends and composites degraded faster than homopolymers. In the spectrum of pure PLA, the intensity of the band at 1750 cm −1 decreases (Supplementary file). Adding natural rubber changes the dependency. In the spectra of all PLA/NR composites, the intensity of the band at 1750 cm −1 increased. This meant that the formation of C=O groups of acids and esters during degradation prevailed over the process of elimination of PLA ester groups when NR added.
The morphologies of the samples also changed. The PLA/NR film composites became muddy. This result was not surprising. Many authors observed a similar effect   [2,3,6,10,45]. It is known that oligomers, dimers, and lactic acid are formed (Figure 8) in the process of PLA hydrolytic degradation, which cause a loss of transparency. Summarizing the results, the influence of microbiota and water, even at ambient temperature, on PLA and PLA/NR composites becomes evident. Despite a low degree of biodegradation, the morphologies and structures of the samples changed, which was recorded by various methods. In the middle of the 20th century, in the works of J.A. Manson, L.H. Sperling, V.N. Kuleznev, and other authors, the features of the structures and the properties of heterogeneous polymer systems were studied. Definitely, these scientists did not work with biodegradable polymers, but, nevertheless, the patterns remained the same. Stresses were formed at the polymer1-polymer2 interface due to different viscosities, thermal expansion coefficients of the components, the chemical nature of the polymers, and other parameters. As a result, very often polymer blends and composites degraded faster than homopolymers.

Conclusions
PLA and PLA/NR film composites with 5, 10, and 15 wt.% NR were obtained and subjected to biotic and hydrolytic degradation at an ambient temperature. From the mentioned results, the following conclusions can be derived: - As it stands, 100% PLA is well hydrolyzed in distilled water, and PLA/NR films are more actively subjected to biotic degradation compared to pure polylactide; - The influence of natural rubber on the structure and thermophysical characteristics of the PLA matrix and on the behavior of PLA/NR composites during degradation is shown; - The morphological observation indicated the surface erosion of all samples both during biotic and hydrolytic degradation; -Differences in the crystal structure of PLA in highly defective and less damaged film regions were detected by the XRD method; -FTIR-ATP spectra demonstrated a significant change in the chemical structure of PLA/NR film composites during hydro-and bio-degradation;

Conclusions
PLA and PLA/NR film composites with 5, 10, and 15 wt.% NR were obtained and subjected to biotic and hydrolytic degradation at an ambient temperature. From the mentioned results, the following conclusions can be derived: - As it stands, 100% PLA is well hydrolyzed in distilled water, and PLA/NR films are more actively subjected to biotic degradation compared to pure polylactide; - The influence of natural rubber on the structure and thermophysical characteristics of the PLA matrix and on the behavior of PLA/NR composites during degradation is shown; - The morphological observation indicated the surface erosion of all samples both during biotic and hydrolytic degradation; -Differences in the crystal structure of PLA in highly defective and less damaged film regions were detected by the XRD method; -FTIR-ATP spectra demonstrated a significant change in the chemical structure of PLA/NR film composites during hydro-and bio-degradation; -Adding NR increases the degree of biodegradation of PLA/NR composites due to the formation of a heterogeneous system and an increase in the proportion of the amorphous phase in the samples.